Increased hydrophilicity and anti-fouling effect of orthokeratology lenses with NVP and PEGMA coating

Plasma-enhanced chemical vapor deposition (PECVD) is a vacuum plasma treatment procedure for the deposition of thin film on a substance, which was first used on orthokeratology lenses (ortho-k lenses) in order to coat polymerized 1-vinyl-2-pyrrolidinone (NVP) and poly(ethylene glycol) methacrylate (PEGMA) on the lenses. First, the surface of ortho-k lenses was pretreated with electrons, radicals, and peroxides for 9 min, under 9 sccm Ar, 36 sccm O2, and 120 W of applied radio frequency (RF) power. NVP and PEGMA were deposited on the surface of lenses through the heating of NVP to 50°C and PEGMA to 43°C.

The chamber pressure was maintained at 300 mTorr, with 40 W of applied RF power, 12 sccm Ar, and an 8-cm treatment distance. Obviously decreased water contact angle of NVP/PEGMA-coated lenses exhibited excellent hydrophilicity, which lasted for up to 90 days, and significant lower protein adsorption was observed on NVP/PEGMA-coated lenses. Besides, the MTT assay revealed the great biocompatibility of the coated lenses. Therefore, the results showed that PECVD can be used to prepare NVP/PEGMA-coated ortho-k lenses with excellent long-lasting hydrophilicity and anti-fouling effect.

Event tip: EC Conference Functional Coatings & Nanotechnology

Discover the future of coating technology! Will functional coatings help us achieve our climate goals? How do nanoscale materials change coating properties? Find out from leading experts at the EC Conference Functional Coatings & Nanotechnology, taking place on April 9th – 10th, 2024 in Cologne. Register now and be part of the discussion on the latest trends and breakthroughs.

If you are interested in more information about the improved hydrophilicity and anti-fouling effect of orthokeratology lenses coated with NVP and PEGMA by plasma-enhanced chemical vapor deposition, the research has been published in the Journal of Coatings Technology and Research.